GEHRY1020-1100 ºC Red paste formulated for 3D printing is designed for manufacturing models with wings or very open angles. With a cylindrical format of 8 cm in diameter, designed to speed up the filling of 3D printers, making the filling process more practical and clean. Firing range: 1020-1100ºC. Water content Drying shrinkage 22 % 9,00 % ºC Weight loss Porosity Firing shrinkage 1020ºC 7,01 % 6,00 % Biscuit fired: 800-850ºC Thermal coefficient: 73.80x10-7ºC-1 (25ºC-500ºC)
Read More
LLOYD1240-1280 ºC High-temperature white paste formulated for 3D printing, designed to manufacture models with shallow layer heights, where high definition and extremely light and delicate pieces are sought. With a cylindrical format of 8 cm in diameter, designed to speed up the filling of 3D printers, making the filling process more practical and clean. Firing range: 1240-1280ºC. Water content Drying shrinkage 22 % 8,08 % ºC Weight loss Porosity Firing shrinkage 1020ºC 1,20 % 11,00 % Biscuit fired: 950-1000ºC Thermal coefficient: 52,80x10-7ºC-1 (25ºC-500ºC)
Read More